一种改性滑石粉及其制备方法和应用

本发明公开了一种改性滑石粉，在滑石粉外包覆有低熔点塑料，具有核-壳包覆结构。

制备方法包括如下步骤：(1)将滑石粉干燥后与表面改性剂在110～120℃下搅拌混合5～30min ... CN102558915A-一种改性滑石粉及其制备方法和应用 -GooglePatents 一种改性滑石粉及其制备方法和应用 DownloadPDF Info Publicationnumber CN102558915A CN102558915A CN2010106139310A CN201010613931A CN102558915A CN102558915A CN102558915A CN102558915A CN2010106139310A CN2010106139310A CN2010106139310A CN201010613931A CN201010613931A CN201010613931A CN102558915A CN102558915A CN102558915A Authority CN China Priorartkeywords talcumpowder preparation modifiedtalc powder talcpowder Priorartdate 2010-12-30 Legalstatus(Thelegalstatusisanassumptionandisnotalegalconclusion.Googlehasnotperformedalegalanalysisandmakesnorepresentationastotheaccuracyofthestatuslisted.) Pending Applicationnumber CN2010106139310A Otherlanguages English(en) Inventor 王敏 许海燕 张靓 姜亮靓 吴驰飞 CurrentAssignee(Thelistedassigneesmaybeinaccurate.Googlehasnotperformedalegalanalysisandmakesnorepresentationorwarrantyastotheaccuracyofthelist.) JiangsuYingnanewmaterialsCo.Ltd. OriginalAssignee SHANGHAIPOLYNANOMATERIALTECHNOLOGYCoLtd Prioritydate(Theprioritydateisanassumptionandisnotalegalconclusion.Googlehasnotperformedalegalanalysisandmakesnorepresentationastotheaccuracyofthedatelisted.) 2010-12-30 Filingdate 2010-12-30 Publicationdate 2012-07-11 2010-12-30 ApplicationfiledbySHANGHAIPOLYNANOMATERIALTECHNOLOGYCoLtd filed Critical SHANGHAIPOLYNANOMATERIALTECHNOLOGYCoLtd 2010-12-30 PrioritytoCN2010106139310A priority Critical patent/CN102558915A/zh 2012-07-11 PublicationofCN102558915A publication Critical patent/CN102558915A/zh Status Pending legal-status Critical Current Links Espacenet GlobalDossier Discuss 239000000843 powder Substances 0.000 title claims abstract description 71 239000000454 talc Substances 0.000 title claims abstract description 71 229910052623 talc Inorganicmaterials 0.000 title claims abstract description 71 235000012222 talc Nutrition 0.000 title claims abstract description 71 238000002360 preparationmethod Methods 0.000 title claims abstract description 12 238000002156 mixing Methods 0.000 claims abstract description 25 239000004033 plastic Substances 0.000 claims abstract description 21 229920003023 plastic Polymers 0.000 claims abstract description 21 239000003795 chemicalsubstancesbyapplication Substances 0.000 claims abstract description 12 238000001035 drying Methods 0.000 claims abstract description 10 238000003756 stirring Methods 0.000 claims abstract description 9 -1 aluminicacidester Chemicalclass 0.000 claims description 15 238000002844 melting Methods 0.000 claims description 11 239000004698 Polyethylene(PE) Substances 0.000 claims description 6 QIQXTHQIDYTFRH-UHFFFAOYSA-N Stearicacid Chemicalcompound data:image/svg+xml;base64,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 data:image/svg+xml;base64,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 CCCCCCCCCCCCCCCCCC(O)=O QIQXTHQIDYTFRH-UHFFFAOYSA-N 0.000 claims description 6 229920000573 polyethylene Polymers 0.000 claims description 6 239000000203 mixture Substances 0.000 claims description 5 239000006087 SilaneCouplingAgent Substances 0.000 claims description 4 229920001684 lowdensitypolyethylene Polymers 0.000 claims description 4 239000004702 low-densitypolyethylene Substances 0.000 claims description 4 235000021355 Stearicacid Nutrition 0.000 claims description 3 239000008117 stearicacid Substances 0.000 claims description 3 238000000034 method Methods 0.000 abstract 1 239000002245 particle Substances 0.000 description 11 239000000945 filler Substances 0.000 description 7 238000005516 engineeringprocess Methods 0.000 description 6 239000000463 material Substances 0.000 description 5 239000011159 matrixmaterial Substances 0.000 description 4 238000005453 pelletization Methods 0.000 description 4 238000003672 processingmethod Methods 0.000 description 4 239000007790 solidphase Substances 0.000 description 4 239000000126 substance Substances 0.000 description 4 239000000969 carrier Substances 0.000 description 3 229920000642 polymer Polymers 0.000 description 3 239000011258 core-shellmaterial Substances 0.000 description 2 239000008187 granularmaterial Substances 0.000 description 2 229920000092 linearlowdensitypolyethylene Polymers 0.000 description 2 239000004707 linearlow-densitypolyethylene Substances 0.000 description 2 230000004048 modification Effects 0.000 description 2 238000006011 modificationreaction Methods 0.000 description 2 239000002861 polymermaterial Substances 0.000 description 2 230000003014 reinforcing Effects 0.000 description 2 238000004381 surfacetreatment Methods 0.000 description 2 241000024287 Areas Species 0.000 description 1 239000004606 Fillers/Extenders Substances 0.000 description 1 238000005411 VanderWaalsforce Methods 0.000 description 1 239000000654 additive Substances 0.000 description 1 230000000996 additive Effects 0.000 description 1 230000015572 biosyntheticprocess Effects 0.000 description 1 238000006243 chemicalreaction Methods 0.000 description 1 239000002131 compositematerial Substances 0.000 description 1 150000001875 compounds Chemicalclass 0.000 description 1 230000000694 effects Effects 0.000 description 1 229920001971 elastomer Polymers 0.000 description 1 239000000806 elastomer Substances 0.000 description 1 238000005755 formationreaction Methods 0.000 description 1 229910052500 inorganicmineral Inorganicmaterials 0.000 description 1 239000011229 interlayer Substances 0.000 description 1 239000010410 layer Substances 0.000 description 1 238000004519 manufacturingprocess Methods 0.000 description 1 239000000155 melt Substances 0.000 description 1 239000011707 mineral Substances 0.000 description 1 239000003607 modifier Substances 0.000 description 1 239000012071 phase Substances 0.000 description 1 230000000704 physicaleffect Effects 0.000 description 1 238000006116 polymerizationreaction Methods 0.000 description 1 230000002787 reinforcement Effects 0.000 description 1 238000005096 rollingprocess Methods 0.000 description 1 238000010008 shearing Methods 0.000 description 1 230000035939 shock Effects 0.000 description 1 239000000758 substrate Substances 0.000 description 1 Abstract 本发明公开了一种改性滑石粉，在滑石粉外包覆有低熔点塑料，具有核-壳包覆结构。

制备方法包括如下步骤：(1)将滑石粉干燥后与表面改性剂在110～120℃下搅拌混合5～30min，得到预处理的滑石粉；混合搅拌的速度为500～1000rpm；(2)将步骤(1)所得到预处理的滑石粉与低熔点塑料在105～110℃下共混10～30min；共混搅拌的速度为1000～1500rpm；滑石粉、表面改性剂和低熔点塑料的重量比为1∶0.1～0.2∶0.01～0.05。

方法不仅工艺简单，易于操作，成本低，能够改善被填充的塑料的各项等力学性能。

Description 一种改性滑石粉及其制备方法和应用 技术领域 [0001] 本发明涉及材料领域，具体为一种用于高分子聚合物填料的滑石粉，尤其是改性滑石粉及制备方法和应用。

背景技术 [0002] 聚合物的增韧，是高分子材料领域一直以来倍受关注的一个问题。

[0003] 聚合物增韧的最主要的方法是加入橡胶类弹性体，制备成聚合物/弹性体二相或聚合物/弹性体/填料多相复合材料。

低模量、低强度橡胶类弹性体作为增韧剂大量加入，在提高了材料的韧性的同时，也造成使得材料的刚性下降。

[0004] 刚性粒子的增韧为这一问题提供了很好的解决方法。

刚性粒子增韧聚合物材料微观形态的特点是：（1)刚性粒子在合物基体中均勻分散；（¾刚性粒子与聚合物基体问存在弹性界面相，这种弹性界面相为刚粒子与聚合物基体间提供了具有一定形变能力的良好界面结合。

[0005] 无机填料在塑料改性中起到重要作用，已成为不可缺少的改性助剂。

在不同的应用领域，滑石粉作为增量剂、增强剂、功能改性剂，已经为业内人士认同。

这与滑石粉本身的特性密不可分：层间的连接力（范德华力）很微弱，使其柔软，降低了加工过程中对设备的磨损性；片层结构可给予填充体系刚度和冲击强度间的最佳平衡；对于有机物具有一定的亲和力；滑石粉表面既有疏水性又有惰性；而且滑石粉具有较高的白度。

[0006] 然而，滑石粉作为填料，与塑料基体之间的相容性差，影响体系的最终性能。

为了改善两者之间的界面有机结合，必须对滑石粉表面进行改性处理。

[0007] 用表面改性剂对滑石粉进行表面改性已经得到了的广泛认可。

为了获得良好的界面，加入表面改性剂后，加入弹性体之后，在均勻分散的刚性粒子周围嵌入非界面化学结合的但能产生强物理缠结的具有一定厚度的柔性界面层，形成软包硬的核-壳结构，从而使体系的晃面粘结明显加强、韧性与强度均有增加。

用填充母粒法制备刚性核-壳结构粒子，通过滑石粉表面处理，使之与弹性体二者物理化学性质相近，并在挤出机螺杆剪切力的作用下，提高滑石粉在载体中的分散程度；选择与基体聚合物有较好相容性的、低粘度的弹性体为载体，通过之前的滑石粉表面处理，载体与滑石粉熔融改性，使物料在挤出机中停留的有限时间内，滑石粉弹性体间发生化学反应或产生物理作用，达到一定界面粘附强度，制备出含有滑石粉弹性体的“核-壳”结构粒子的聚合物材料。

[0008] 但是利用弹性体制备这样一种核壳粒子的问题在于弹性体的成本较高，可能会限制这样一种填充母粒的应用前景。

目前国内还没有用低熔点塑料对滑石粉进行包覆的专利报道。

发明内容 [0009] 本发明旨在提供一种改性滑石粉。

[0010] 本发明还提供了这种改性滑石粉的制备方法。

[0011] 本发明的另一个目的是将这种改性滑石粉用作聚合物的填料。

[0012] 一种改性滑石粉，在滑石粉外包覆有低熔点塑料，具有核-壳包覆结构。

[0013] 这种改性滑石粉的制备方法为，包括如下步骤： [0014] (1)将滑石粉干燥后与表面改性剂在110〜120°C下搅拌混合5〜30min，得到预处理的滑石粉；混合搅拌的速度为500〜IOOOrpm； [0015] (2)将步骤⑴所得到预处理的滑石粉与低熔点塑料在105〜110°C下共混10〜30min；共混搅拌的速度为1000〜1500rpm； [0016] 所用的原料组分滑石粉、低熔点塑料和表面改性剂的重量比为1：0.1〜0.2：0.01〜0.05。

[0017] 所用述的表面改性剂选自铝酸酯、钛酸酯、硅烷偶联剂或硬脂酸中的至少一种。

铝酸酯可选自DL-411、DL-411-AF或DL-411-D，钛酸酯可选用NXT-201或NXT-401，硅烷偶联剂可选用KH-550、KH560或KH570。

上述各种表面改性剂可以单独使用，也可以混合使用。

[0018] 所述的低熔点塑料选自低密度聚乙烯或线形低密度聚乙烯，这些低熔点的塑料聚合度一般为为40到1500。

[0019] 本发明采用熔融共混技术，对滑石粉进行表面改性，得到一种具有新型核-壳包覆结构的改性滑石粉粒子。

该方法不仅工艺简单，易于操作，而且使用低熔点的塑料取代了弹性体，成本上也有很大的优势。

[0020] 这种熔融共混方法对操作的要求低，通过熔融共混使滑石粉与低熔点塑料形成了良好的核-壳包覆结构。

所得到的改性滑石粉利于填充塑料粒子，能够改善被填充的塑料的各项等力学性能，并且降低了塑料的成本，利于环保。

具体实施方式 [0021] 实施例1 [0022] (1)取滑石粉IOkg干燥后，与铝酸酯（DL-411，南京道宁化工有限公司）0.2kg在120°C下用高混机以700rpm的速度搅拌20min混勻，得到预处理的滑石粉，取出备用； [0023] (2)取1.8kg低熔点聚乙烯LDPE，与步骤（1)所得预处理过的滑石粉在105°C下用高混机以1400rpm的速度熔融共混15min，得到改性滑石粉。

[0024] (3)取步骤O)的改性滑石粉13kg，与87kg回收PP(聚丙烯）混勻，经过低温固相加工方法挤出造粒。

产品性能见表1。

[0025] 双螺杆挤出机一区温度为130°C，二区温度为150°C，三区温度为150°C，四区温度为180°C，五区温度为180°C，六区温度为200°C，七区温度为210°C，机头温度为200°C；螺杆转速为120rpm。

[0026] 实施例2 [0027] (1)取滑石粉IOkg干燥后，与0.Ikg钛酸酯（NXT-401，南京翔飞化学研究所)和0.Ikg的硬脂酸在120°C下用高混机以700rpm的速度搅拌20min混勻，得到预处理的滑石粉，取出备用； [0028] (2)取1.8kg低熔点聚乙烯LDPE，干燥后与步骤（1)所得预处理过的滑石粉在105°C下用高混机以1400rpm的速度熔融共混15min，得到改性滑石粉。

[0029] (3)取步骤（¾制备的改性滑石粉13kg，与87kg回收PP混勻，经过低温固相加工方法挤出造粒。

挤出的工艺同实施例1。

产品性能见表1。

[0030] 实施例3 [0031] (1)取滑石粉IOkg干燥后，与铝酸酯（DL-411-AF，南京道宁化工有限公司）0.2kg在120°C下用高混机以700rpm的速度搅拌20min混勻，得到预处理的滑石粉，取出备用； [0032] (2)取1.8kg线形低熔点聚乙烯LLDPE，干燥后与步骤⑴所得预处理过的滑石粉在105°C下用高混机以1400rpm的速度熔融共混15min，得到改性滑石粉。

[0033] (3)取步骤（¾制备的改性滑石粉13kg，与87kg回收PP混勻，经过低温固相加工方法挤出造粒。

挤出的工艺同实施例1。

产品性能见表1。

[0034] 实施例4 [0035] (1)取滑石粉IOkg干燥后，与硅烷偶联剂（KH-550，深圳市成企商贸有限公司）0.2kg在120°C下用高混机以700rpm的速度搅拌20min混勻，得到预处理的滑石粉，取出备用； [0036] (2)取1.8kg线形低熔点聚乙烯LLDPE，干燥后与步骤⑴所得预处理过的滑石粉在105°C下用高混机以1400rpm的速度熔融共混15min，得到改性滑石粉。

[0037] (3)取步骤（¾制备的改性滑石粉13kg，与87kg回收PP混勻，经过低温固相加工方法挤出造粒。

挤出的工艺同实施例1。

产品性能见表1。

[0038] 表1 [0039] Claims(7) 1. 一种改性滑石粉的制备方法，其特征在于，包括如下步骤：(1)将滑石粉干燥后与表面改性剂在Iio〜120°C下搅拌混合5〜30min，得到预处理的滑石粉；(2)将步骤（1)所得到预处理的滑石粉与低熔点塑料在105〜110°C下共混10〜30min；所用的原料组分中，滑石粉、低熔点塑料和表面改性剂的重量比为1：0.1〜0.2：0.01〜0.05。

2.权利要求1所述一种改性滑石粉的制备方法，其特征在于，所述表面改性剂选自铝酸酯、钛酸酯、硅烷偶联剂或硬脂酸中的至少一种。

3.权利要求1所述一种改性滑石粉的制备方法，其特征在于，所述的低熔点塑料选自分子量为400〜1500的低密度聚乙烯或线形低密度聚乙烯。

4.权利要求1所述一种改性滑石粉的制备方法，其特征在于，步骤（1)中混合搅拌的速度为500〜IOOOrpm0 5.权利要求1所述一种改性滑石粉的制备方法，其特征在于，步骤（2)中共混搅拌的速度为1000〜1500rpm。

6. 一种改性滑石粉，其特征在于，通过权利要求1〜5所述的方法制备，具有核-壳包覆结构。

7.权利要求6所述改性滑石粉作为填充剂在制备改性塑料方面的应用。

CN2010106139310A 2010-12-30 2010-12-30 一种改性滑石粉及其制备方法和应用 Pending CN102558915A (zh) PriorityApplications(1) ApplicationNumber PriorityDate FilingDate Title CN2010106139310A CN102558915A (zh) 2010-12-30 2010-12-30 一种改性滑石粉及其制备方法和应用 ApplicationsClaimingPriority(1) ApplicationNumber PriorityDate FilingDate Title CN2010106139310A CN102558915A (zh) 2010-12-30 2010-12-30 一种改性滑石粉及其制备方法和应用 Publications(1) PublicationNumber PublicationDate CN102558915A true CN102558915A (zh) 2012-07-11 Family ID=46405590 FamilyApplications(1) ApplicationNumber Title PriorityDate FilingDate CN2010106139310A Pending CN102558915A (zh) 2010-12-30 2010-12-30 一种改性滑石粉及其制备方法和应用 CountryStatus(1) Country Link CN (1) CN102558915A (zh) CitedBy(7) *Citedbyexaminer,†Citedbythirdparty Publicationnumber Prioritydate Publicationdate Assignee Title CN102964679A (zh) * 2012-10-31 2013-03-13 安徽省易达电子有限公司 一种含有改性滑石粉的电容器薄膜及其制备方法 CN104119609A (zh) * 2014-07-02 2014-10-29 合肥和安机械制造有限公司 一种汽车线束聚丙烯护套材料用改性滑石及其制备方法 CN104592791A (zh) * 2014-12-31 2015-05-06 安徽恒昊科技有限公司 一种硅处理滑石粉的制备方法 CN104989890A (zh) * 2015-07-17 2015-10-21 四川省川杭塑胶科技有限公司 埋地排水排污用双层增强改性聚烯烃drpo波纹管 CN106380627A (zh) * 2016-08-31 2017-02-08 泉州市旭丰粉体原料有限公司 一种刚韧平衡改性滑石粉的制备方法及应用 CN110845765A (zh) * 2019-12-06 2020-02-28 扬州海吉科技有限公司 一种疏水功能包覆的颗粒材料及其制备方法 CN112442289A (zh) * 2020-11-10 2021-03-05 桂林桂广申巴粉体材料有限责任公司 一种改性滑石粉、其制备方法及应用 Citations(12) *Citedbyexaminer,†Citedbythirdparty Publicationnumber Prioritydate Publicationdate Assignee Title JPH02169644A (en) * 1988-10-21 1990-06-29 BpChemInternatlLtd Productionofchargedwater-crosslinkablesilanecopolymercomposition JPH052165A (ja) * 1991-02-19 1993-01-08 ToshibaLighting&TechnolCorp 照明装置 CN1211591A (zh) * 1998-07-16 1999-03-24 中山大学 无机填料增韧、增强聚丙烯复合物及其制备方法 CN1215068A (zh) * 1998-06-18 1999-04-28 中国科学院化学研究所 一种增韧聚烯烃用填充母粒及其制备方法和用途 RU2180907C2 (ru) * 1999-11-24 2002-03-27 Москoвcкийгосударственныйуниверситетприкладнойбиотехнологии Эпоксиднаякомпозициядляпокрытий JP3380300B2 (ja) * 1993-08-10 2003-02-24 三菱化学株式会社 自動車インストルメントパネル用樹脂組成物 CN1400252A (zh) * 2001-08-01 2003-03-05 上海杰事杰新材料股份有限公司 一种改性沥青组合物及其制备方法 CN1970647A (zh) * 2006-12-08 2007-05-30 海城市精华微粉厂 一种复合改性剂表面改性滑石粉体的制备方法 US20070142537A1 (en) * 2000-12-15 2007-06-21 EdwardsWalterL MethodsforMakingPolyesterResinsHavingReducedFrictionalProperties CN101735526A (zh) * 2008-11-18 2010-06-16 中国石油天然气股份有限公司 一种改性高抗冲聚苯乙烯组合物及其制备方法 CN101746547A (zh) * 2008-12-08 2010-06-23 中国石油天然气股份有限公司 改性沥青包装薄膜袋及其制备方法 WO2010149546A1 (en) * 2009-06-22 2010-12-29 BorealisAg Stabilizedpolypropylene-talccomposite 2010 2010-12-30 CN CN2010106139310A patent/CN102558915A/zh active Pending PatentCitations(12) *Citedbyexaminer,†Citedbythirdparty Publicationnumber Prioritydate Publicationdate Assignee Title JPH02169644A (en) * 1988-10-21 1990-06-29 BpChemInternatlLtd Productionofchargedwater-crosslinkablesilanecopolymercomposition JPH052165A (ja) * 1991-02-19 1993-01-08 ToshibaLighting&TechnolCorp 照明装置 JP3380300B2 (ja) * 1993-08-10 2003-02-24 三菱化学株式会社 自動車インストルメントパネル用樹脂組成物 CN1215068A (zh) * 1998-06-18 1999-04-28 中国科学院化学研究所 一种增韧聚烯烃用填充母粒及其制备方法和用途 CN1211591A (zh) * 1998-07-16 1999-03-24 中山大学 无机填料增韧、增强聚丙烯复合物及其制备方法 RU2180907C2 (ru) * 1999-11-24 2002-03-27 Москoвcкийгосударственныйуниверситетприкладнойбиотехнологии Эпоксиднаякомпозициядляпокрытий US20070142537A1 (en) * 2000-12-15 2007-06-21 EdwardsWalterL MethodsforMakingPolyesterResinsHavingReducedFrictionalProperties CN1400252A (zh) * 2001-08-01 2003-03-05 上海杰事杰新材料股份有限公司 一种改性沥青组合物及其制备方法 CN1970647A (zh) * 2006-12-08 2007-05-30 海城市精华微粉厂 一种复合改性剂表面改性滑石粉体的制备方法 CN101735526A (zh) * 2008-11-18 2010-06-16 中国石油天然气股份有限公司 一种改性高抗冲聚苯乙烯组合物及其制备方法 CN101746547A (zh) * 2008-12-08 2010-06-23 中国石油天然气股份有限公司 改性沥青包装薄膜袋及其制备方法 WO2010149546A1 (en) * 2009-06-22 2010-12-29 BorealisAg Stabilizedpolypropylene-talccomposite CitedBy(11) *Citedbyexaminer,†Citedbythirdparty Publicationnumber Prioritydate Publicationdate Assignee Title CN102964679A (zh) * 2012-10-31 2013-03-13 安徽省易达电子有限公司 一种含有改性滑石粉的电容器薄膜及其制备方法 CN102964679B (zh) * 2012-10-31 2015-06-17 安徽省易达电子有限公司 一种含有改性滑石粉的电容器薄膜及其制备方法 CN104119609A (zh) * 2014-07-02 2014-10-29 合肥和安机械制造有限公司 一种汽车线束聚丙烯护套材料用改性滑石及其制备方法 CN104592791A (zh) * 2014-12-31 2015-05-06 安徽恒昊科技有限公司 一种硅处理滑石粉的制备方法 CN104989890A (zh) * 2015-07-17 2015-10-21 四川省川杭塑胶科技有限公司 埋地排水排污用双层增强改性聚烯烃drpo波纹管 CN104989890B (zh) * 2015-07-17 2017-05-03 四川省川杭塑胶科技有限公司 埋地排水排污用双层增强改性聚烯烃drpo波纹管 CN106380627A (zh) * 2016-08-31 2017-02-08 泉州市旭丰粉体原料有限公司 一种刚韧平衡改性滑石粉的制备方法及应用 CN106380627B (zh) * 2016-08-31 2019-01-04 泉州市旭丰粉体原料有限公司 一种刚韧平衡改性滑石粉的制备方法及应用 CN110845765A (zh) * 2019-12-06 2020-02-28 扬州海吉科技有限公司 一种疏水功能包覆的颗粒材料及其制备方法 CN112442289A (zh) * 2020-11-10 2021-03-05 桂林桂广申巴粉体材料有限责任公司 一种改性滑石粉、其制备方法及应用 CN112442289B (zh) * 2020-11-10 2021-09-14 桂林桂广申巴粉体材料有限责任公司 一种改性滑石粉、其制备方法及应用 SimilarDocuments Publication PublicationDate Title CN102558915A (zh) 2012-07-11 一种改性滑石粉及其制备方法和应用 EP2285879B1 (en) 2017-07-26 Improvedconductivityofresinmaterialsandcompositematerials CN103613883B (zh) 2016-01-13 一种以石墨烯为填料的耐磨损硬质复合材料及其制备方法 CN103374162B (zh) 2015-08-05 增韧、增刚双功能填充母粒及其制备方法 CN102585348A (zh) 2012-07-18 一种增韧导电材料及其制备方法 CN103113730B (zh) 2017-02-01 一种聚乳酸复合材料及其制备方法 CN100429270C (zh) 2008-10-29 高冲击强度聚苯乙烯增刚增韧填充母料的制备方法 CN102453404A (zh) 2012-05-16 一种新型聚乙烯粉末涂料 CN102675819A (zh) 2012-09-19 一种耐磨自润滑聚甲醛及其制备方法 KR20050098945A (ko) 2005-10-12 불소수지복합체조성물 CN103483680A (zh) 2014-01-01 聚丙烯长碳链尼龙共混物及其制备方法 CN102337021A (zh) 2012-02-01 一种用于选择性激光烧结的尼龙复合粉末材料 CN102827408A (zh) 2012-12-19 一种聚烯烃增强增韧母料及其生产方法 CN1793213A (zh) 2006-06-28 Eva(乙烯－醋酸乙烯共聚物)发泡填充母料的制备方法 CN103275448B (zh) 2015-05-06 一种改性填料离子增强型聚四氟乙烯复合材料的制备方法 CN107129630A (zh) 2017-09-05 一种导电/抗静电pp基木塑复合材料及其制备方法 CN102675818A (zh) 2012-09-19 一种增强增韧聚甲醛及其制备方法 CN101805524B (zh) 2011-09-14 高温耐储存的废橡胶粉改性沥青的制备方法 CN103249769A (zh) 2013-08-14 包含聚(芳基醚酮)和石墨烯材料的聚合物组合物 CN102838806A (zh) 2012-12-26 一种低密度高流动性高模量聚丙烯及其制备方法 CN1191300C (zh) 2005-03-02 聚丙烯/弹性体/无机填料三元复合材料及其制备方法 KR101620668B1 (ko) 2016-05-12 탄소나노물질함유수지조성물및플라스틱성형품 CN101402812B (zh) 2012-05-09 一种导电热塑性粉末及其制备方法和应用 CN102453405A (zh) 2012-05-16 一种新型聚丙烯粉末涂料 US20130030117A1 (en) 2013-01-31 Methodofmanufacturingpolyamideandcarbonnanotubecompositeusinghighshearingprocess LegalEvents Date Code Title Description 2012-07-11 C06 Publication 2012-07-11 PB01 Publication 2012-09-12 C10 Entryintosubstantiveexamination 2012-09-12 SE01 Entryintoforceofrequestforsubstantiveexamination 2014-05-28 ASS Successionorassignmentofpatentright Ownername: JIANGSUYINGNANEWMATERIALCO.,LTD. Freeformattext: FORMEROWNER:SHANGHAIPOLYNANOMATERIALTECHNOLOGYCO.,LTD. Effectivedate: 20140505 2014-05-28 C41 Transferofpatentapplicationorpatentrightorutilitymodel 2014-05-28 COR Changeofbibliographicdata Freeformattext: CORRECT:ADDRESS;FROM:200237XUHUI,SHANGHAITO:226500NANTONG,JIANGSUPROVINCE 2014-05-28 TA01 Transferofpatentapplicationright Effectivedateofregistration: 20140505 Addressafter: 226500JiangsucityofNantongprovinceRugaoCityZhenDengvillagefifteengroupheadNo.6 Applicantafter: JiangsuYingnanewmaterialsCo.Ltd. Addressbefore: 200237MeilongRoad,Shanghai,No.130,No. Applicantbefore: ShanghaiPolynanoMaterialTechnologyCo.,Ltd. 2015-01-14 C12 Rejectionofapatentapplicationafteritspublication 2015-01-14 RJ01 Rejectionofinventionpatentapplicationafterpublication Applicationpublicationdate: 20120711